DESLON66
DSC201GH6 NT
| Molding method | Injection molding |
|---|---|
| Features | Rigidity, Dimensional Stability, Surface Appearance, Moldability |
| Ingredients | PA66 GF30% |
-
Ingredients
Material characteristicsDESLON® DSC201GH6 NT is a Polyamide66 product with 30% Glass Fiber reinforcement, offering excellent mechanical stiffness and heat resistance.
Molding conditionMoisture in resin can cause decomposition during the injection molding process, leading to property degradation and molding defects. To prevent this, it is essential to dry the resin in a dehumidifying dryer at a minimum temperature of 100°C for at least 4 hours prior to molding. This process ensures that the moisture content is reduced to below 0.2%, thereby preventing these issues
-
Application Part
Interior
Industrial Products
-
Application Examples
| Property | Item | Condition | Method | Unit | Value |
|---|---|---|---|---|---|
| Physical | Water Absorption | 23°C, 50% RH | ASTM D570 | % | |
| Specific Gravity | 23°C | ASTM D792 | - | 1.36 | |
| Mold shrinkage | Flow, 60 X 60 X 2mm | ASTM D955 | % | ||
| Cross-flow, 60 X 60 X 2mm | ASTM D955 | % | |||
| Mechanical | Tensile Strength | 5 mm/min(Reinforced), 50mm/min(Unreinforced), 3.2mm | ASTM D638 | kgf/cm2 | 1900 |
| Elongation | 5 mm/min(Reinforced), 50mm/min(Unreinforced), 3.2mm | ASTM D638 | % | 3 | |
| Flexural Strength | 5.6 mm/min(Reinforced), 16.8mm/min(Unreinforced) 6.4mm | ASTM D790 | kgf/cm2 | 97000 | |
| Flexural Modulus | 5.6 mm/min(Reinforced), 16.8mm/min(Unreinforced) 6.4mm | ASTM D790 | kgf/cm2 | 3000 | |
| Izod Impact Strength | Noched, 6.4mm, 23°C | ASTM D256 | kgf.cm/cm | 15 | |
| Rockwell Hardness | R-Scale | ASTM D785 | - | 121 | |
| Thermal | Melting Point | ASTM D3418 | °C | 259 | |
| HDT(1.8MPa) | 6.4mm, Edgewise, Unannealed | ASTM D648 | °C | 247 | |
| HDT(0.46MPa) | 6.4mm, Edgewise, Unannealed | ASTM D648 | °C | 260 | |
| Flammability | UL 94 | - | HB | ||
| Electrical | Volume resistivity | ASTM D257 | Ohm | ||
| Dielectric Constant(10^6HZ) | ASTM D150 | - | |||
| Dielectric Strength | ASTM D149 | KV/mm | |||
| ARC resistance | ASTM D495 | Sec |
| Property | Unit | Range | |
|---|---|---|---|
| Resin Drying Temperature | °C | 100~120 | |
| Resin Drying Time | Hr | 4~5 | |
| Cylinder | Rear | °C | 270~280 |
| Middle | °C | 280~285 | |
| Front | °C | 285~290 | |
| Nozzle Temperature | °C | 280~285 | |
| Resin Temperature | °C | 280~285 | |
| Molding Temperature | °C | 80~120 | |
| Speed | % | 40~70 | |
| Pressure | 1st | % | 30~60 |
| 2nd | % | 30~60 | |
| Holding Pressure | % | 10~20 |